    Impact response of nanoparticle reinforced 3D woven spacer/epoxy composites at cryogenic temperatures
    (Sage Publications Ltd, 2021) Yildirim, Ferhat; Tatar, Ahmet Caner; Eskizeybek, Volkan; Avci, Ahmet; Aydin, Mustafa
    Fiber-reinforced polymer composites serving in harsh conditions must maintain their performance during their entire service. The cryogenic impact is one of the most unpredictable loading types, leading to catastrophic failures of composite structures. This study aims to examine the low-velocity impact (LVI) performance of 3D woven spacer glass-epoxy composite experimentally under cryogenic temperatures. LVI tests were conducted under various temperatures ranging from room temperature (RT) to -196 degrees C. Experimental results reveal that the 3D composites gradually absorbed higher impact energies with decreasing temperature. Besides, the effect of multi-walled carbon nanotube and SiO2 nanofiller reinforcements of the matrix on the impact performance and the damage characteristics were further assessed. Nanofiller modification enhanced the impact resistance up to 30%, especially at RT. However, the nanofiller efficiency declined with decreasing temperature. The apparent damages were visually examined by scanning electron microscopy to address the damage formation. Significant outcomes have been achieved with the nanofiller modification regarding the new usage areas of 3D woven composites.
  • Küçük Resim Yok
    Öğe
    Improved mechanical performance of three-dimensional woven glass/epoxy spacer composites with carbon nanotubes
    (Sage Publications Ltd, 2021) Yildirim, Ferhat; Aydin, Mustafa; Avci, Ahmet
    Three-dimensional polymer composites offer various features and design options due to their hollow structure and lightweight. However, to exploit their advantages, it is a must to improve their structural features and mechanical performances including out-plane direction. Although introducing thermoplastic fillers between the plies or multilayered design addresses on this critical issue, the benefits offered by the nanoparticles with superior mechanical properties come a step forward as an another engineering solution. Based on this motivation, the goal of this study is to investigate the impact of multiwalled carbon nanotubes on the mechanical and thermomechanical performances of three-dimensional woven glass/epoxy spacer composites. Therefore, multiwalled carbon nanotubes at various content were introduced into epoxy matrix, and the multiwalled carbon nanotubes-epoxy mixture was infused to three-dimensional woven fabric with the vacuum-assisted resin transfer method. The obtained results indicated that the three-point bending strength and modulus were enhanced up to 25 and 80% for warp direction and enhanced up to 44 and 85% for weft direction with carbon nanotube addition, respectively. Tensile strength developed in the warp direction by 7%, while the strength value in the weft direction did not change. The tensile strain values for warp and weft directions enhanced up to 19 and 12% with carbon nanotube addition, respectively. In addition, thermomechanical analysis has revealed that the glass transition temperature and storage modulus were also improved. Particle dispersion detection with color measurement and scanning electron microscopy analyses revealed the effectiveness of the ultrasonic mixing on the dispersion of carbon nanotubes in the epoxy matrix. The consequences of carbon nanotube addition on microscale morphology were discussed based on the fracture morphologies to nanoscale and microscale toughening mechanisms in the existence of carbon nanotube reinforcement.