Effect of in-/ex-situ annealing temperature on the optical, structural and gas sensing dynamics of CdS nanostructured thin films
Küçük Resim Yok
Tarih
2020
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Academic Press Ltd- Elsevier Science Ltd
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Effect of in-/ex-situ annealing on the structure, optical, photoluminescence, electrical characterization and gas sensing dynamics on CdS thin films are presented. Raman characterizations showed an increase in the peak intensity with increasing the annealing temperature under ex-situ, while a lower peak intensity observed through the in-situ annealing condition. No shift was observed in the Photoluminescence peaks through the yellow band peaks of in-situ annealed samples, however, a slightly blue shift was observed through the ex-situ annealed samples. High conductivity was observed for all samples, while in the case of in-situ RT, in-situ 100 degrees C, ex-situ 200 degrees C and ex-situ 300 degrees C, a CO2 and O-2 gas sensing activity have been tested. The ex-situ 300 degrees C sample shows a higher response towards CO2 compared with the ex-situ 200 degrees C film. While, both in-situ RT and 100 degrees C sensors show the same response towards CO2 with a high gas response. However, the in-situ 100 degrees C sensor has the highest response compared to in-situ RT film with a high response of 25% at 50 sccm towards O-2.
Açıklama
Anahtar Kelimeler
Cds, In-Situ And Ex-Situ Annealing, Nanostructured Thin Film, Gas Sensor
Kaynak
Superlattices And Microstructures
WoS Q Değeri
Q3
Scopus Q Değeri
Q2
Cilt
142