Effect of ZrSiO4 on the corrosion behavior of MgO-FeAl2O4 composite refractory materials
Küçük Resim Yok
Tarih
2016
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Carl Hanser Verlag
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this study, the corrosion behavior of refractory materials that were produced by incorporating ZrSiO4 (zircon) at different ratios into MgO-FeAl2O4 (hercynite) were investigated. The values of density and open porosity of those samples were also measured, and the corrosion behaviors of those materials produced were examined. After performing corrosion tests, the corrosion resistance of composite refractory materials were determined by measuring the penetration distances and spreading areas. The incorporation of ZrSiO4 into MgO-FeAl2O4 generally decreased the porosity of composite refractory materials, and consequently reduced the penetration distances and spreading area values of the corroded regions of refractories as well. In addition, the formation of new phases and the microstructural changes which occurred were determined by XRD measurements and SEM analyses. On the basis of microstructural characterization carried out in the interface of clinkerrefractory, the following observations had been determined: i) Ca2+ and Y3+ elements forming CaZrO3 were located together in the same regions, ii) forsterite phase was formed due to the reaction between SiO2, which is released after dissociation of zircon as ZrO2 and SiO2 during sintering, and MgO, iii) the formation of new CaZrO3 and forsterite (Mg2SiO4) phases made a barrier effect against clinker, and iv) the amount of CaO decreased based on the EDX analysis made from clinker to refractory in a corroded region. The penetration of clinker to refractory showed a minimum level for the composition of MgO-5 wt.-% FeAl2O4-5 wt.-% ZrSiO4 and an improvement by about 38 % as compared to MgO-5 wt.-% FeAl2O4. This improvement is associated with a long service life of MgO-FeAl2O4-ZrSiO4 refractories for industrial applications.
Açıklama
Anahtar Kelimeler
Refractory Elements, Composite Materials, Mgo, Zrsio4, Feal2o4, Corrosion, Cazro3
Kaynak
Materials Testing
WoS Q Değeri
Q4
Scopus Q Değeri
Q2
Cilt
58
Sayı
11.Ara