The effects of stacking sequence on drilling machinability of filament wound hybrid composite pipes: Part-2 damage analysis and surface quality
Küçük Resim Yok
Tarih
2020
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Elsevier Sci Ltd
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In the first part of this two-part study, filament wound hybrid composite pipes with various stacking sequences were manufactured and mechanical properties such as hardness, ring tensile strength, and burst strength were experimentally investigated. After determining mechanical properties, drilling tests were performed to research machinability characteristics. The second part of the study consists damage analysis and surface quality examination including ring test damage analysis, push-out delamination analysis, borehole damage examination and borehole surface quality. The experimental data suggested that cutting parameters, stacking sequence, and the use of back-up were impactful on the formation and propagation of various types of damages. Especially, the effect of stacking sequence was remarkable. A larger delamination area was formed in Glass-Glass-Carbon (GGC) sample after the ring tensile tests compared to Glass-Carbon-Glass (GCG) and Carbon-Glass-Glass (CGG) samples. In all cases, the utilization of back-up lead to decrease of delamination with 9-40% reduction in surface roughness. When the back-up is not used during drilling, an excessive push-out delamination occurred in all drilling tests. Moreover, CGG samples represented lower push out delamination. In addition, position of the hole depending on the winding angle plays a key role on damage formation and surface quality.
Açıklama
Anahtar Kelimeler
Hybrid Composite Pipes, Composite Tubes, Delamination, Damage Analysis, Drilling Machinability, Stacking Sequence, Surface Quality
Kaynak
Composite Structures
WoS Q Değeri
Q1
Scopus Q Değeri
Q1
Cilt
235