Halloysite nanotube reinforcement endows ameliorated fracture resistance of seawater aged basalt/epoxy composites
Küçük Resim Yok
Tarih
2020
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Sage Publications Ltd
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Seawater aging-dominated delamination failure is a critical design parameter for marine composites. Modification of matrix with nanosized reinforcements of fiber-reinforced polymer composites comes forward as an effective way to improve the delamination resistance of marine composites. In this study, we aimed to investigate experimentally the effect of halloysite nanotube nanoreinforcements on the fracture performance of artificial seawater aged basalt-epoxy composites. For this, we introduced various amounts of halloysite nanotubes into the epoxy and the halloysite nanotube-epoxy mixtures were used to impregnate to basalt fabrics via vacuum-assisted resin transfer molding, subsequently. Fracture performances of the halloysite nanotubes modified epoxy and basalt/epoxy composite laminated were evaluated separately. Single edge notched tensile tests were conducted on halloysite nanotube modified epoxy nanocomposites and the average stress intensity factor (K-IC) was increased from 1.65 to 2.36 MPa.m(1/2) (by 43%) with the incorporation of 2 wt % halloysite nanotubes. The interlaminar shear strength and Mode-I interlaminar fracture toughness (G(IC)) of basalt-epoxy hybrid composites were enhanced from 36.1 to 42.9 MPa and from 1.22 to 1.44 kJ/m(2), respectively. Moreover, the hybrid composites exhibited improved seawater aging performance by almost 52% and 34% in interlaminar shear strength and G(IC) values compared to the neat basalt-epoxy composites after conditioning in seawater for six months, respectively. We proposed a model to represent fracture behavior of the seawater aged hybrid composite based on scanning electron microscopy and infrared spectroscopy analyses.
Açıklama
Anahtar Kelimeler
Halloysite Nanotube, Basalt Fiber, Seawater Aging, Fracture Toughness, Mechanical Test
Kaynak
Journal Of Composite Materials
WoS Q Değeri
Q3
Scopus Q Değeri
Q2
Cilt
54
Sayı
20