The effect of Ti to the crystal structure of Li7-3xMxLa3Zr1.8Ti0.2O12 (M= Ga, In) garnet-type solid electrolytes as a second dopant
(Taylor & Francis, 2023) Saran, Sevda; Eker, Yasin Ramazan; Ateş, Şule; Çelik, Gültekin; Baveghar, Hadi; Özkendir, Osman Murat; Atav, Ülfet; Klysubun, Wantana
Garnet-type solid-state electrolytes are promising candidates for solid-state lithium batteries, nevertheless their ionic conductivity is still not enough for commercial applications. On the other hand, doping still is the common way to improve the ionic conductivities of these solid electrolytes. In this study, mono and dual-doped garnet-type solid electrolytes were synthesised by substituting indium (In), gallium (Ga), indium-titanium (In-Ti) and gallium-titanium (Ga-Ti) to the Li7La3Zr2O12 structure by a solid-state reaction method. The contribution of substitutions to the formation of crystal phases was investigated by X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS). On the other hand, morphological analyses were done by scanning electron microscope (SEM) and the ionic conductivities of the solid electrolytes were determined by electrochemical impedance spectroscopy (EIS). The study showed that while Li7-3xInxLa3Zr2O12 (for x = 0.05, 0.10, 0.15, 0.20) and Li7-3xGaxLa3Zr2O12 (for x = 0.05) samples were formed in tetragonal phase with a space group of I41/acd:2, dual substituted Li7-3xInxLa3Zr1.8Ti0.2O12 and Li7-3xGaxLa3Zr1.8Ti0.2O12 solid electrolytes for all x values were formed in cubic phase with a space group of I-43d. The highest conductivity is reached for Li6.85Ga0.05La3Zr1.8Ti0.2O12. The radial distribution function studies showed that when more In and Ga atoms take place in the sites of Li atoms, more O atoms take place in the vicinity of both substituted In and Ga atoms within the Li7La3Zr1.8Ti0.2O12 (LLZTO) crystal framework which can eventuate in a change in the conduction mechanism.
Wear behavior of in-situ oxide dispersion strengthened Fe-8Ni alloy with Zr additions
(Chulalongkorn University, 2023) Tekin, Mustafa; Muhaffel, Faiz; Kotan, Hasan; Baydoğan, Murat
In this study, in-situ oxide dispersion strengthened (ODS) Fe91Ni8Zr1 and Fe88Ni8Zr4 alloys were produced by combination of high energy mechanical alloying (HEMA) and high temperature equal channel angular extrusion (HT-ECAE). The wear behaviors of the consolidated samples were investigated under different loads from 1 N to 4 N by reciprocating wear tests at room temperature. The Scanning electron microscopy (SEM) was used to examine the wear tracks to analyze the wear characteristics as a function of applied loads. The relative comparison of the wear results showed that under the lower loads of 1 N and 2 N, Fe88Ni8Zr4 alloy has lower wear rate than Fe91Ni8Zr1 alloy whereas under the higher loads of 3 N and 4 N, it is vice versa. Additionally, the friction coefficient of Fe91Ni8Zr1 alloy was found to be lower than that of Fe88Ni8Zr4 alloy under all the applied loads. The results were comparatively discussed with respect to microstructural features of 1 at% Zr and 4 at% Zr containing ODS alloys produced by HEMA followed by ECAE. The obtained results of ODS alloys with different grain size, precipitate size, and number density of the precipitates, may disclose a new sight for using such alloys in wear applications just as cutting tools, turbine blades, and discs.
Next generation 2D materials for anodes in battery applications
(Elsevier, 2023) Kumar, Madhu Raj; Singh, Sangeeta; Fahmy, Heba Mohamed; Jaiswal, Neeraj K.; Akın, Seçkin; Shalan, Ahmed Esmail; Lanceros-Mendez, Senentxu; Salado, Manuel
Two-dimensional (2D) materials, for instance, graphene/graphene derivatives, transition metal-dichalcogenides (TMDs), and MXenes (e.g. transition metal carbides (TMCs) as well as nitrides (TMNs)) are under increasing research attention due to their unique physical, mechanical, magnetic, electrical, optical, and chemical prop-erties. They are explored for a variety of applications, including energy generation and storage systems. Notwithstanding the developing interest in these materials, with respect to the later area, there is an absence of comprehensive overview and analysis on the synthesis and application of 2D materials aimed at lithium (Li) ion batteries. In this review, we have gathered and discussed the main issues faced by the different methods involved in the synthesis of 2D inorganic materials and their composites, along with their main properties in addition to applications for lithium, sodium (Na), and potassium (K) ion batteries. In addition, the problems raised during the charging and discharging of batteries for those materials are also discussed and possible proposed solutions are also included here. Overall, this review provides a road-map on current demands and future research di-rections on 2D materials to address the critical limitations of Li, Na and K ion batteries, for the afterward generation of high-performance energy storage systems.
Bakır alttaşa yapılan ön işlemin tek tabaka grafen film kalitesine etkisi
(2016) Yılmaz, Mücahit; Eker, Yasin Ramazan
Tekdüze büyük ölçekli grafen tabakaları sentezlemek için çeşitli metotlar önerilmiştir. Bunlardan en çok tercih edileni bakır veya nikel alttaş üzerine kimyasal buhar biriktirme (CVD) yöntemiyle grafen büyütmektir. Son çalışmalarda, kusursuz formasyona sahip tek tabaka grafenin, bakırın kristal yapısına kritik bir şekilde bağlı olduğu bilinmektedir. Bu etkinin yanı sıra, bakır alttaşa yapılan ön işlemin de grafen oluşumunu etkilediği düşünülmüştür. Çalışmada alttaş olarak 25 ?m kalınlıklı bakır folyolar standart temizleme, elektroliz ile parlatma ve tavlama gibi üç farklı ön işlemden geçirilmiştir. Daha sonra metan (CH4) ve hidrojen (H2) proses gazları kullanılarak grafen sentezlenmiştir. Bakır folyonun yapısı ve kalitesi XRD ve XRF ile belirlenmiştir. Büyütme işleminden sonra bakır alttaşların üst yüzeyleri ve alt yüzeyleri Konfokal Raman kullanılarak incelenmiş, oluşan grafenin özellikleri tespit edilmiştir. Sonuç olarak elektroliz ile parlatma ön işleminden geçirilmiş bakır alttaş üzerinde, tek tabaka grafen oluşumu gözlenirken diğer ön işlemlerden geçirilmiş bakır alttaşlar üzerinde çok tabakalı grafenler gözlenmiştir.
Recovery of waste tyres by pyrolysis in a fixed bed reactor for liquid fuel production: effects of pyrolysis conditions on oil yield
(2017) Hopa, Derya Yeşim; Yılmaz, Alime; Aksoy Bahtlı, Tuba
One of the major environmental problems around the world is disposal of waste tyres without any purpose. Disposal of waste tyres is an increasing environmental problem. Also because of high content of valuable chemicals and other compounds hidden in the waste tyres, disposal of them is an economical problem as well. Pyrolysis is a thermochemical process that can be used for recovery of the valuable chemicals in the waste tyre. Pyrolysis is a recycling process in which, liquid product can be used as a fuel directly or can be mixed with petroleum refined oils. Derived gaseous product can also be used as a fuel and solid product can be considered as a fuel and low grade carbon black. In this work, granulated waste tyres have been pyrolyzed in a fixed bed reactor under different conditions of temperature, heating rate and inert purging gas (N2) flow rate. The purpose of the study was to optimize the pyrolysis parameters in order to produce the highest amount of oil. 400C, 450C and 500C were selected and the maximum yield of liquid product was observed at 450C. Among the heating rates of 10C/min, 15C/ min and 20C/min; 10C/min was the parameter that gave maximum oil yield. And while working at 450C and 10C/min; N2(g) flow rate was examined by using 0.5 L/min, 1 L/min and 1.5 L/min. The maximum oil yield was observed at 1 L N2(g) /min. According to the results of the study; at 450C, with a heating rate of 10C/min and 1 L N2(g)/min gave the maximum yield of oil, which is 53.33 wt. The pyrolytic oil from waste tyre had the Gross Calorific Value of 42.6 MJ/kg which is very close to that of commercial diesel no 2 (around 42-46 MJ/kg). The pyrolytic oil produced is a promising fuel and can be used as a source of energy after some future work for make it suitable for use in vehicles or in other areas like factories or houses etc.
Kükürt ve Kül Giderimi Yapılmış Pirolitik Karbon Siyahı Katkılı MgO-C Refrakterlerin Mekanik Özelliklerinin İncelenmesi
(2017) Bahtlı, Tuba; Bostancı, Veysel Murat; Hopa, Derya Yeşim; Yalçın Yastı, Şerife
Lastik atıklarının refrakter sektöründe geri kazanımını sağlamak amacı ile yapılan bu çalışmada, piroliz reaktöründe 500 C sıcaklık, 15 C/dk ısıtma hızı ve 0,5L/dk N2 akış hızı parametrelerinde elde edilen katı ürünün kükürt ve kül miktarları azaltılmış ve daha sonrasında MgO-C refrakter malzemelerinin üretiminde karbon kaynağı olarak kullanılmıştır. Üretilen refrakterlerin yoğunluk, % açık gözenek ve soğuk basma mukavemeti (SBM) değerlerinin kükürt ve kül miktarı ile değişimi incelenmiştir. Piroliz sonrası atık lastiğin ve kükürt ve kül giderimi sonrası elde edilen pirolitik karbon siyahı malzemelerinin X-Işını Difraktometresi (XRD) ile faz analizleri, taramalı elektron mikroskobu (SEM) ile mikroyapı analizleri ve Enerji Dağılımlı X-Işını Analizi (EDX) ile kimyasal analizleri gerçekleşmiştir. Kükürt ve kül miktarları azaldıkça, bu ürünlerin kullanıldığı refrakter malzemelerin % açık gözenek miktarının ve yoğunluk değerlerinin yaklaşık aynı olmasına rağmen soğuk basma mukavemeti değerlerinin arttığı görülmüştür.
Lastik Atığının Pirolizi İle Elde Edilen Karbon Siyahı Kullanılarak Üretilen MgO-C Refrakter Tuğlanın Fiziksel ve Mekanik Özelliklerine Kükürt Miktarının Etkisi
(2017) Bahtlı, Tuba; Bostancı, Veysel Murat; Hopa, Derya Yeşim; Yalçın Yastı, Şerife
Her geçen gün miktarı artan lastik atıklarının sebep olduğu problemleri önlemek ve refrakter sektöründe geri kazanımını sağlamak amacı ile yapılan bu çalışmada, piroliz parametrelerine bağlı olarak pirolitik karbon siyahı içerisindeki kükürt miktarının değişimi ve ayrıca, pirolitik katı ürün olan karbon siyahı kullanılarak üretilen MgO-C refrakter malzemelerinin yoğunluk, açık gözenek ve soğuk basma mukavemeti değerlerinin kükürt miktarı ile değişimi incelenmiştir. Kükürt miktarının azalması ile yoğunluk ve SBM değerlerinin arttığı, açık gözenek değerlerinin ise azaldığı gözlenmiştir.
Bronz ve dökme demir talaşlarının geri dönüştürülmesiyle prizmatik şekilli makine elemanı üretimi ve mekanik karakterizasyonu
(2018) Aslan, Abdullah; Salur, Emin; Aydın, Güneş; Şahin, Ömer Sinan; Karadağ, Hakan Burak; Akdemir, Ahmet
Bu çalışmada küresel grafitli dökme demir (GGG-40) ve Bronz (CuSn10) talaşlarının izostatik sıcakpresleme yöntemiyle geri dönüştürülmesi ile üretilen metal matrisli kompozit malzemelerin (MMK) üretimive mekanik davranışları incelenmiştir. MMK malzemeler 4 farklı karışım oranında 3 farklı sıcaklıkta ve 3farklı basınçta üretilerek üretim parametrelerinin gözeneklilik, sertlik ve eğilme mukavemeti üzerine etkisiincelenmiştir. Prizmatik geometrili olarak üretilen numunelerin öncelikle gözeneklilik ve yoğunluk değerleritespit edilmiştir. Daha sonra Brinell ve Mikro Vickers ve 3 noktadan eğilme deneyleri ile MMKmalzemelerin mukavemeti belirlenmiştir. Optik mikroskopi tekniği ile mikro yapı görüntüleri incelenerektalaşların birleşme mekanizması incelenmiştir. Ayrıca XRD analizi aracılığıyla metalik talaşlar arasında arafaz oluşumu olup olmadığı sorgulanmıştır. Gözeneklilik deneyleri neticesinde %20 mertebelerindegözeneklilik elde edilmiştir. Aşırı plastik deformasyon gösteren CuSn10 sebebiyle mukavemeti artanCuSn10 talaşları sertlik değerini Bulk CuSn10 ile kıyaslanabilir seviyelere getirmiştir. Eğilme deneyineticesinde MMK malzemelerin eğilme mukavemetleri bulk CuSn10’dan düşük çıkmıştır. Sonuç olarakmetal talaşların başarılı bir biçimde metal matris kompozit haline getirilebileceği gösterilmiştir.
Termal kararlılığı arttırılmış demir esaslı ferritik çelik tozlarının sıcak pres ve sıcak ekstrüzyon (ECAE) yöntemleri ile konsolidasyonu
(2016) Kotan, Hasan
Bilyeli değirmenler ile üretilen yüksek mukavemetli tozların konsolidasyonunda temel hedef mekanik özelliklerinde önemli bir kayıp olmadan bu tozların birleştirilerek porozite içermeyen ürüne dönüştürülebilmesidir. Son yıllarda yapılan araştırmalar sıcak ekstrüzyon ile yüksek kayma ve basınca maruz bırakılan tozların porozite içermeden, teorik yoğunluklarında birleştirilebileceğini göstermiştir. Bu çalışmada sıcak presleme ve yüksek sıcaklıklarda çok geçişli eş kanallı açısal ekstrüzyon (ECAE - equal channel angular extrusion) teknikleri kullanılarak nano-kristalin Fe-Ni-Zr tozlarından konsolide edilmiş ferritik alaşımların üretimi araştırılmıştır. Elde edilen sonuçlar sıcak presleme metodu ile teorik yoğunluğa ulaşılamadığını, ancak sıcak ekstrüzyon yöntemi ile yapısında porozite içermeyen ve teorik yoğunlukta malzeme üretilebileceğini göstermiştir. Konsolidasyon sonucunda mikroyapıda mikrometre seviyelerine ulaşan tane büyümesi gözlenmesine rağmen üretilen bu çeliklerin sertliği 4-6 GPa civarındadır.
AH Plus’ın geleneksel yöntem ya da PIPS aktivasyonu ile uygulanan yıkama solüsyonlarıyla muamele edilmiş kök dentini yüzeyini ıslatabilirliği
(2018) Akbulut, Makbule Bilge; Terlemez, Arslan; Batıbay, Ahmet Burçin
Amaç: Bu in vitro çalışmanın amacı; epoksi rezin içerikli kökkanal patının (AH Plus) sodyum hipoklorit (NaOCl), klorheksidin glukonat (CHX), etilendiamintetraasetik asit (EDTA) yıkama solüsyonlarının geleneksel yöntemle ya da foton indüklüfotoakustik dalgalanma (PIPS) aktivasyon tekniğiyle uygulandığı dentin yüzeyini ıslatabilirliğini değerlendirmektir. Gereç ve Yöntem: Bu çalışma için 60 adet tek köklü diş hazırlandı ve dişler silikon ölçü maddesi içerisine sabitlendi. Silikonsertleştikten sonra dişler bukkolingual yönde dikey olarak ikiparçaya ayrıldı. Bir yarım diş örneği tekrar silikon içerisine yerleştirildi. Örnekler 6 deney grubuna ayrıldı (n10) ve şu yıkama prosedürleri uygulandı: Grup 1, NaOCl; Grup 2, CHX; Grup3, EDTA; Grup 4, NaOClPIPS; Grup 5, CHXPIPS; Grup 6, EDTAPIPS. İşlem görmeyen diğer yarım diş örneklerinden rastgele seçilen 10 tanesi kontrol grubu olarak kullanıldı ve distilesu içerisinde bekletildi. Bir damla kök kanal patı her bir kuru dentin yüzeyine damlatıldı. Kanal patı ve kök dentini arasındaki temas açısı dinamik temas açısı ölçüm cihazıyla belirlendi. Veriler, tek yönlü varyans analizi ile istatistiksel olarak analiz edildi. Bulgular: Ortalama temas açısı değerleri NaOCl grubunda60.93, CHX grubunda 57.77, EDTA grubunda 64,61 olup deney grupları ve kontrol grubunun temas açıları arasında istatistiksel olarak anlamlı fark bulunmamıştır (p0,05). Yıkamasolüsyonlarının PIPS ile aktivasyonu AH Plus’ın ıslatma davranışını değiştirmemiştir (p 0,05). Sonuç: Bu in vitro çalışmanın sınırları dahilinde yıkama solüsyonunun türü ve uygulama metodu AH Plus’ın ıslatma davranışını etkilememiştir.
Effect of Impactor Mass on Dynamic Response and Retention Properties of Composite Plates under Successive Impacts
(2016) Karadağ, Hakan Burak; Şahin, Ömer Sinan; Güneş, Aydın
This study mainly focuses on the effect of mass of impactor upon dynamic response of laminated composites. For this purpose two different impactors with different masses were used. The impact velocities were selected so that impactors with different masses had the same kinetic energy. The experiments were performed on simply supported woven E-glass reinforced epoxy laminates which are made of 8 layers stacked symmetrically. The variation of impact force, impactor velocity and laminate displacement versus interaction time were obtained. The impulse and energy absorption characteristics and damage zones were also investigated. After low velocity impact, the test specimens were subjected to three-point bending testing in order to get retention mechanical properties.